[1]刘英伟,张洋,董雪峰.铸件凝固后期液膜抗拉能力分析[J].哈尔滨工程大学学报,2019,40(06):1182-1186.[doi:10.11990/jheu.201804001]
 LIU Yingwei,ZHANG Yang,DONG Xuefeng.Tensile ability of liquid film in the later stage of casting solidification[J].hebgcdxxb,2019,40(06):1182-1186.[doi:10.11990/jheu.201804001]
点击复制

铸件凝固后期液膜抗拉能力分析(/HTML)
分享到:

《哈尔滨工程大学学报》[ISSN:1006-6977/CN:61-1281/TN]

卷:
40
期数:
2019年06期
页码:
1182-1186
栏目:
出版日期:
2019-06-05

文章信息/Info

Title:
Tensile ability of liquid film in the later stage of casting solidification
作者:
刘英伟1 张洋1 董雪峰2
1. 哈尔滨工程大学 材料科学与化学工程学院, 黑龙江 哈尔滨 150001;
2. 伍伦贡大学, 机械、材料、机电一体化和生物医学工程系, 新南威尔士 2522
Author(s):
LIU Yingwei1 ZHANG Yang1 DONG Xuefeng2
1. School of Materials Science and Chemical Engineering, Harbin Engineering University, Harbin 150001, China;
2. School of Mechanical, Materials, Mechatronics and Biomedical Engineering, University of Wollongong, New South Wales 2522, Australia
关键词:
凝固表面张力附加压力热裂晶粒晶界曲率半径抗拉能力
分类号:
TG21
DOI:
10.11990/jheu.201804001
文献标志码:
A
摘要:
金属凝固后期是热裂纹产生的危险期,晶粒之间的液膜对热裂有一定的抵抗作用,研究液膜的抗拉能力的影响因素,无疑对提高铸件的质量有着积极意义。本文采用微积分方法建立了液膜抗拉能力与曲率半径的解析式,通过质量守恒条件推导了液膜曲率半径与晶粒边界间距的关系,从而间接建立了液膜抗拉能力和晶粒边界距离的关系。对以上解析关系的分析表明:在没有液态金属补充的情况下,液膜抵抗能力与液膜表面曲率半径有关,而液膜的曲率半径随晶粒边界间距的增加而变小,并存在一个极值,但此极值和现有文献的结果不同,此时液膜抗拉能力达到最大,如果凝固时收缩拉力不超过此极值,则晶粒不会产生热裂纹,这为凝固工艺的制定提供了重要参考。

参考文献/References:

[1] 陈德平, 许健, 杨刚, 等. 不同浇注方式下铸造风机主轴的热裂模拟及工艺优化[J]. 金属铸锻焊技术, 2011, 40(7):54-56, 62.CHEN Deping, XU Jian, YANG Gang. Simulation of hot tearing of fan main shaft casting under different pouring methods and its process optimization[J]. Casting·forging·welding, 2011, 40(7):54-56, 62.
[2] 谢正茂, 阎顺祥, 赵小军, 等. NT缸体铸造裂纹产生原因分析[J]. 热加工工艺, 2017, 46(5):243-247.XIE Zhengmao, YAN Shunxiang, ZHAO Xiaojun, et al. Analysis on causes of casting cracks in NT cylinder block[J]. Hot working technology, 2017, 46(5):243-247.
[3] 虞强, 彭家锋, 刘国江. 铸造起重机吊具横梁裂纹原因及改造措施[J]. 机电工程技术, 2017, 46(8):203-205.YU Qiang, PENG Jiafeng, LIU Guojiang. The reasons and measures of casting crane beam crack[J]. Mechanical & electrical engineering technology, 2017, 46(8):203-205.
[4] 宋平, 常伟, 苑英伟, 等. 5083铝合金大规格扁锭铸造热裂纹缺陷的研究[J]. 有色金属加工, 2016, 45(5):22-25.SONG Ping, CHANG Wei, YUAN Yingwei, et al. Study of hot cracking in casting of large-size 5083 aluminum alloy ingot[J]. Nonferrous metals processing, 2016, 45(5):22-25.
[5] 石照夏, 董建新, 张麦仓. 汽车增压器涡轮用铸造高温合金热裂研究进展[J]. 材料工程, 2012, 40(6):91-96.SHI Zhaoxia, DONG Jianxin, ZHANG Maicang. Development of hot tearing on cast superalloys used for auto turbocharger turbine wheel[J]. Journal of materials engineering, 2012, 40(6):91-96.
[6] XU Rongfu, ZHENG Hongliang, LUO Jie, et al. Role of tensile forces in hot tearing formation of cast Al-Si alloy[J]. Transactions of nonferrous metals society of China, 2014, 24(7):2203-2207.
[7] 祖方遒, 袁晓光, 梁维中. 铸件成形原理[M]. 北京:机械工业出版社, 2013:28-29.
[8] 刘文君, 蒋斌, 杨青山. 双辊铸造热裂形成及工艺控制[J]. 材料导报A:综述篇, 2011, 25(9):126-130.LIU Wenjun, JIANG Bin, YANG Qingshan. Hot tearing formation and control in twin-roll casting[J]. Materials review, 2011, 25(9):126-130.

相似文献/References:

[1]刘永涛,马宁,顾解忡.三维大幅晃荡的Youngs-VOF法模拟[J].哈尔滨工程大学学报,2012,(09):1075.[doi:10.3969/j.issn.1007-7043. 201109006]
 LIU Yongtao,MA Ning,GU Xiechong.3-D simulation of large amplitude liquid sloshing using Youngs-VOF method[J].hebgcdxxb,2012,(06):1075.[doi:10.3969/j.issn.1007-7043. 201109006]

备注/Memo

备注/Memo:
收稿日期:2018-04-01。
基金项目:中央高校基本科研业务费专项基金(HEUCFP201850).
作者简介:刘英伟,男,副教授.
通讯作者:刘英伟,E-mail:Lywbanner@163.com.
更新日期/Last Update: 2019-06-03